Superhydrophilic polyethersulfone (PES) membranes with high scale inhibition properties obtained through bionic mineralization and RTIPS.

Reverse thermally induced separation (RTIPS) was used to obtain a separation membrane with a better internal structure for a higher water flux and a surface that could easily form a hydration layer. In comparison to the traditional modification method, this work focused on the aspect that the internal structure obtained by changing the membrane-making method provided easier adhesion conditions for the dopamine/TiO2 hybrid nanoparticles (DA/TiO2 HNPs) obtained by biomimetic mineralization. It provided a basis for exploring the variation in adhesion with the water bath temperature and the amount of titanium added through the study of turbidity point, SEM images, water contact angle, thermogravimetric test, EDX, AFM, XPS, FTIR and other test results. The SEM images proved that the membrane obtained through the RTIPS method had a porous surface and spongy internal structure, furthermore, additional polymers were adsorbed. Use of EDX demonstrated that biomimetic mineralization prevented the production of agglomerated titanium dioxide. XPS and FTIR spectra confirmed the introduction and immobilization of HNP aggregation. Moreover, a decrease in the surface roughness and water contact angle further suggested an improvement in the hydrophilicity of the modified membrane. The introduction of HNP at a higher water bath temperature helped increase the water flux up to ten times, moreover, the oil-water separation efficiency could still reach over 99.50%. Lastly, a cycle test of the modified membrane under the optimal conditions helped confirm that the membrane forming conditions at this time could provide a better environment for the formation of the hydrophilic layer, which was conducive to the recycling of the separation membrane. In summary, more fixed more hydrophilic particles could be obtained through the RTIPS method based on biomimetic mineralization to prevent the accumulation of titanium dioxide, thus helping improve permeability and anti-fouling of the membrane.

Bimetallic polyphenol networks structure modified polyethersulfone membrane with hydrophilic and anti-fouling properties based on reverse thermally induced phase separation method.

In order to improve the hydrophobicity of traditional polyethersulfone (PES) membranes, this study combined the reverse thermally induced phase separation (RTIPS) method with the constructed bimetallic polyphenol networks (BMPNs) to prepare hydrophilic anti-fouling membranes. As for BMPNs, tannic acid (TA) was served as an intermediate to construct both the inner and surface hydrophilic layers of the PES membranes. On the one hand, etching Zeolitic imidazolate framework-8 (EZIF-8) with synergistic etching and surface functionalization via TA not only retained the high pore structure of MOFs, but also had good hydrophilicity. On the other hand, the MPN hydrophilic layer was formed on the membrane surface by the combination of TA from the surface of EZIF-8 and iron ions in the coagulation bath. Therefore, BMPNs structure penetrated the interior and surface of PES membrane, which greatly improved the hydrophilic properties. In addition, the membrane with porous surfaces and spongy cross sections by RTIPS method improved the permeability and mechanical properties of the membrane by several times compared with the membrane via NIPS method. The obtained membranes in this experiment showed excellent permeability, just like pure water flux reached 1662.16 L/m2 h, while BSA rejection rate remained at 92.78%. Compared with pure membrane, it showed a better flux recovery rate (FRR = 83.33%) after cleaning, and the reduction of irreversible (Rir = 16.67%) fouling indexes indicated that the adsorption of protein was inhibited. These results suggested that the hydrophilic anti-fouling PES membranes prepared by this method possessed great application potential in membrane separation technology.

Development of hydrophilic PES membranes using F127 and HKUST-1 based on the RTIPS method: Mitigate the permeability-selectivity trade-off.

In this study, to mitigate the permeability-selectivity trade-off effect, Pluronic F127 (F127) and HKUST-1 were employed to construct high-performance membranes based on the reverse thermally induced phase separation (RTIPS) method. F127, as a hydrophilic modifier, was applied to increase permeability and resist polyethersulfone (PES) membrane fouling, while the collapse of HKSUT-1 caused by its instability in pure water improved the permeability and selectivity of the membrane. Characterizations demonstrated the successful synthesis of HKUST-1, together with the successful introduction of HKSUT-1 and F127 in PES membranes. It was observed that the membrane prepared by the RTIPS process possessed a uniformly porous surface and sponge-like cross-section with excellent mechanical properties, higher permeability, and selectivity compared to the dense skin and finger-like cross-section of the membrane prepared by the nonsolvent induced phase separation (NIPS) method. Moreover, the permeation and bovine serum albumin (BSA) rejection rate of the optimal membrane reached 2378 L/m2 h and 89.3%, respectively, which were far higher than those of the pure membrane. Hydrophilic F127 and many microvoids formed by the collapse of HKUST-1, played an important role in excellent antifouling properties, high permeability, and selectivity by pure water flux (PWF), flux recovery rate (FRR), BSA flux, and COD removal rate tests. Overall, the membrane with F127 and HKSUT-1 prepared via the RTIPS method not only obtained excellent antifouling properties but also mitigated the permeability-selectivity trade-off.